2019年12月1日 · Polyacrylonitrile (PAN) membranes have been prepared using needleless electrospinning with wire electrode and characterized by a series of methods HRSEM, XRD, air permeability and area weight measurements in dependence of …

2019年1月19日 · 入了解 pan 纤维的内在本质和指导工业生产。 本 从图中可以发现 :各聚丙烯腈纤维的 X 射线衍射图 θ 文拟通过 X 射线衍射中的二维衍射图像与 2 扫描 中在赤道线方向某些特定区域都有强烈的并且非常 法 ,解析不同种类 PAN 纤维的微细结构。

Experiment revealed great changes in degree of alignment, crystallization, exothermic peak, and mechanical properties of nanofibers. ... PAN nanofibers after hot-drawing treatment developed well,...

The differential scanning calorimetry (DSC), Fourier Transform Infrared Spectrometer (FTIR), X-ray diffraction (XRD), and Thermogravimetric Analysis (TG) characterization have been applied to ...

XRD pattern for PAN polymer is shown in Figure 2, which exhibits intense peaks at 2θ = 17° and a small one at 29° belong to (100) and (300) planes respectively.

先用静电纺丝法制备聚丙烯腈 (PAN)、聚乙烯醇 (PVA)和聚乙烯吡咯烷酮 (PVP)基高分子纤维，然后将其碳化制备出不同碳源的多孔碳纤维材料。 使用X-射线衍射仪、红外光谱仪、差示扫描量热仪和N2吸脱附分析仪等手段表征了碳纤维材料的结构和性能。 结果表明，PAN基碳纤维的比表面积最大 (113.5 m2/g)、微孔较多，对刚果红的吸附量最大 (560.2 g/kg)。 根据吸附动力学模型和吸附等温线的分析结果，碳纤维对刚果红的吸附属单层吸附。 结果还表明，温度越高材料的吸附 …

通过组合差热分析，热重分析和xrd分析研究了聚丙烯腈（pan）的热降解。 根据实验观察，已经提出腈基团到共轭聚亚胺结构的分子内聚合起初仅限于PAN的无定形区，其几乎没有废气的逸出。

2010年12月31日 · 聚丙烯腈（PAN）以其良好结构性能，已被许多研究者用作制备炭膜的前驱体材料。从宏观反应上分析，PAN在热解过程中发生了环化、交联、链断裂反应，小分子链段的断裂和析出形成了PAN炭膜的7L结构”。

通过全谱拟合法对碳纤维制备过程中不同阶段纤维的xrd谱图进行处理,得到不同阶段纤维的微观结构参数,研究了聚丙烯腈(pan)基碳纤维制备过程中晶态结构的演变.全谱拟合法基于晶体衍射的严格物理理论,拟合目标为整个衍射谱,并不是个别衍射峰,所得结果具有更 ...

文中采用静电纺丝装置制备了纳米PAN纤维,并对静电纺丝形成过程和影响因素进行了探讨,研究了聚合物溶液浓度、静电压和喷射速率对纳米纤维形貌、直径及结晶情况的影响,并考察了纳米纤维的热稳定性．为纳米碳纤维的制备奠定了基础．. PAN,分子量30 000,金山石化;N,N-二甲基甲酰胺 (DMF),分析纯 (上海润捷化学试剂有限公司)．.