Graphene oxide (GO) and reduced graphene oxide (RGO) are known to have superior properties for various applications. This work compares the properties of GO and RGO with graphite. GO was...

2014年8月1日 · Reduction of the commercial graphene oxide (FL-RGOc) leads to: (i) smaller about 8 nm × 1 nm (average diameter and height) graphene stacking nanostructure with a smaller distance between planes, i.e. 0.4 nm (XRD) (in graphite is 0.335 nm), (ii) 2–3 (XRD) and 4 (REELS) graphene layers in a stacking nanostructure, (iii) decreased content of C ...

2018年2月23日 · Graphite oxide (GO) is produced by modified Hummers’ method and reduced thermally at 250 °C for 1 h in Argon atmosphere to obtain rGO. Self-standing rGO film is prepared via vacuum filtration....

6 天之前 · The XRD patterns of 3DP rGO and rGO/diamane microlattice aerogels are shown in Figure 2e. The main peak of rGO at 26.2° is attributed to (002) crystal plane of graphene. The main peak of rGO at 26.2° is attributed to (002) crystal plane of graphene.

From the XRD patterns of the rGO samples displayed in Fig. 4b, dominant and broad peaks at approximately 2 θ = 24.5° were observed with a d-spacing of around 0.36 nm, which indicated a slight difference when compared to the natural graphite samples (0.336 nm). These findings demonstrated that the crystalline structure can be restored after ...

2018年5月1日 · Hydrothermal reduction is a promising approach for graphene oxide (GO) reduction since it is environmentally friendly, simple, and cost effective. We present a detailed study of...

Download scientific diagram | XRD patterns of graphene oxide (GO) and reduced graphene oxide (rGO). from publication: Improved Performance of CuFe2O4/rGO Nanohybrid as an Anode Material for...

2025年3月30日 · 3.1 Structural properties. Figure 1 shows the powder XRD patterns of GO, rGO, GOH-0, GOH-2, GOH-4, GOH-6, and GOH-8 samples. The (001) and (100) planes of graphene oxide are represented by the sharp and the minor peaks at 11.3° and 42.6°, respectively, in the XRD scan of GO (Fig. 1) [].The XRD scan confirmed that the thermal treatment reduced the amount of GO (Fig. 1).

2019年12月12日 · The optical, structural, and morphological properties of RGO-intercalated GO (RGO/GO) nano-hybrid were studied using UV–Visible spectroscopy, X-ray diffraction, and scanning electron microscopy, respectively. The reduction …

1 天前 · 在 c₄n/rgo 的 hrtem 图像中也观察到了间距为 0.365 nm 的晶面(图 2f)，与 xrd 中的 (002) 晶面相对应。原位生长在 rgo 上的 c₄n 的结晶度优于单独生长的 c₄n 和 c₄n/kb，这可能是二维 rgo 的模板效应所致。